Resumo em Inglês:

Widely used in dentistry, Ti-6Al-4V alloy is difficult to cast and solder, as it frequently exhibits pores inside the structure. This study was conducted to evaluate the effect of joint openings and diameters of laser-welded joints executed in Ti-6Al-4V structures on the presence of pores as checked by radiographic procedures. Sixty dumbbell rods with central diameters of 1.5, 2.0 and 3.5 mm were created from Ti-6Al-4V-wrought bars. Specimens were sectioned and welded using two joint openings (0.0 and 0.6 mm). The combination of variables created six groups (n = 10). Laser welding was executed using 360V/8ms (1.5 and 2.0 mm) and 380V/9ms (3.5 mm), with the focus and frequency set to zero. The joints were finished, polished and submitted to radiographic examination. The radiographs were visually examined for the presence of pores in the joints, qualitatively. The percentage of radiographic presence of pores was calculated without counting pores per joint. Data were analyzed using a chi-square test (α = 0.05). For the 1.5-mm specimens, the incidence of pore presence was significantly higher (p = 0.0001) when using 0.6-mm joint openings (40%) compared to 0.0-mm openings (0%). For the 2.0-mm specimens, there was no significant difference between groups (p = 0.2008). However, for the 3.5-mm specimens, the incidence of pore presence was lower (p = 0.0061) for 0.6-mm openings (50%) compared to 0.0-mm openings (70%). Therefore, laser welding of Ti-6Al-4V structures with thin diameters provides the best condition for the juxtaposition of the parts.

Resumo em Inglês:

The purpose of this study was to evaluate the dentin shear bond strength of four adhesive systems (Adper Single Bond 2, Adper Prompt L-Pop, Magic Bond DE and Self Etch Bond) in regards to buccal and lingual surfaces and dentin depth. Forty extracted third molars had roots removed and crowns bisected in the mesiodistal direction. The buccal and lingual surfaces were fixed in a PVC/acrylic resin ring and were divided into buccal and lingual groups assigned to each selected adhesive. The same specimens prepared for the evaluation of superficial dentin shear resistance were used to evaluate the different depths of dentin. The specimens were identified and abraded at depths of 0.5, 1.0, 1.5 and 2.0 mm. Each depth was evaluated by ISO TR 11405 using an EMIC-2000 machine regulated at 0.5 mm/min with a 200 Kgf load cell. We performed statistical analyses on the results (ANOVA, Tukey and Scheffé tests). Data revealed statistical differences (p < 0.01) in the adhesive and depth variation as well as adhesive/depth interactions. The Adper Single Bond 2 demonstrated the highest mean values of shear bond strength. The Prompt L-Pop product, a self-etching adhesive, revealed higher mean values compared with Magic Bond DE and Self Etch Bond adhesives, a total and self-etching adhesive respectively. It may be concluded that the shear bond strength of dentin is dependent on material (adhesive system), substrate depth and adhesive/depth interaction.

Resumo em Inglês:

This study evaluated fracture torque by torsion, in relation to the length and diameter of orthodontic mini-implants, to demonstrate their viability for clinical and experimental use based on the torque recommended by the manufacturers. The fractures at the moment of insertion, whose incidence in the literature is around 4%, are principally due to excessive force and the inability of the implant to resist rotational forces. Thirty orthodontic mini-implants of three commercial brands available in Brazil (Neodent 1.6 x 9 mm, Dentoflex 1.6 x 9 mm and Kopp 1.6 x 9 mm) were attached to a device made specifically for this research, leaving the mini-implants with sufficient stability. The miniimplants were submitted to torsion torque, using a digital torque wrench, until their breaking point. The values obtained with the test were submitted to analysis of variance and the Tukey test. The mean values of mini-implant ruptures were 26 N.cm for group A (Dentoflex), 25.4 N. cm for group B (Kopp) and 32.8 N.cm for group C (Neodent). From the Tukey test we could observe that the relationships between the means of the Dentoflex and Neodent groups, and between the Kopp and Neodent groups, were significant. Between the Dentoflex and Kopp groups, significance was nonexistent. All the values found in our research for fracture torque were higher than the limits recommended by the manufacturers for clinical use in orthodontics. The highest values were found in the Neodent group.

Resumo em Inglês:

Proper occlusion depends on the correct width ratio between upper and lower teeth, known as Bolton's ratio. In fact, this ratio can be calculated for each pair of teeth from the central incisor to the first permanent molar. This set of ratios, known as comprehensive cumulative percentage ratios (CPRs), can be used not only to determine which tooth or teeth have a tooth width discrepancy, but can also enable the partial graphical analysis of tooth width discrepancy when there is agenesis of certain permanent teeth. Although CPRs have been calculated for Caucasians, tooth width is known to vary depending on racial origin. Therefore, a test of differences between racial groups should be carried out. If these ratios of the Caucasians and Bangkokians are significantly different, the ratio of the Bangkokians is recommended. The objective of this study was to measure tooth size disproportion for Thai patients and to calculate a corresponding set of CPRs. Thirty-seven pairs of dental models were made from a group of Bangkok residents with normal occlusion. Mesiodistal tooth width was measured for each model. The intra- and inter-examiner measurement errors were ascertained as insignificant (p > 0.05). CPRs were then calculated and compared to those derived from other studies. Ten of thirteen CPRs were significantly different from corresponding values derived from Caucasians. We conclude that tooth width ratios vary between different racial groups, and therefore that these should be calculated specifically for each patient racial group.

Resumo em Inglês:

This study evaluated the effect of heat treatment on CrNi stainless steel orthodontic archwires. Half of forty archwires of each thickness - 0.014" (0.35 mm), 0.016" (0.40 mm), 0.018" (0.45 mm) and 0.020" (0.50 mm) (totalling 160 archwires) - were subjected to heat treatment while the remainder were not. All of the archwires had their individual thickness measured in the anterior and posterior regions using AutoCad 2000 software before and after compressive and tensile strength testing. The data was statistically analysed utilising multivariance ANOVA at a 5% significance level. All archwires without heat treatment that were subjected to tensile strength testing presented with anterior opening, which was more accentuated in the 0.020" archwires. In the posterior region, the opening produced by the tensile force was more accentuated in the archwires without heat treatment. There was greater stability in the thermally treated archwires, especially those subjected to tensile strength testing, which indicates that the heat treatment of orthodontic archwires establishes a favourable and indispensable condition to preserve the intercanine width.

Resumo em Inglês:

The aim of this study was to evaluate the depth of curing of 10 contemporary blue light-activated dental flowable materials at several opacities, influenced by different irradiation times using FT-IR spectroscopy. Fifty-five specimens (n = 5) with a 5-mm diameter and 1-mm thickness of translucent (Opallis Flow T), yellowed (Master Flow A2; Opallis Flow A2; Natural Flow A2; Fluroshield Yellowed), and opaque materials (Master Flow OA2; Natural Flow O; Opallis Flow OA3.5; Opallis Flow OP; Fluroshield White) were obtained at six curing times (10s, 20s, 30s, 40s, 50s, and 60s) using a high-intensity LED (Coltolux, Coltène/Whaledent). The degree of conversion (DC) (%) was obtained using the Nexus 470 FTIR Spectrometer (Nicolet Instruments, USA). The FTIR-ATR spectra for uncured and cured samples were analyzed using a ZnSe crystal. The top and bottom surfaces of the cured specimens were analyzed to obtain the depth of curing. Two-way ANOVA was used to analyze the data. The highest curing depth was obtained by Natural Flow OA2, while the lowest was shown by Master Flow OA2. The shortest curing time generated similar depths of cure in comparison with the most extensive for Opallis Flow A2 and Fluroshield Yellowed. Therefore, depth of curing, influenced by the irradiation time, was dependent on the materials. Using the Natural Flow OA2 opaque sealant and the 10-s curing time for Opallis Flow A2 and Fluroshield Yellowed may represent alternative approaches to sealing tooth fissures.

Resumo em Inglês:

The influence of socioeconomic factors and self-rated oral health on children's dental health assistance was assessed. This study followed a cross-sectional design, with a multistage random sample of 792 12-year-old schoolchildren from Santa Maria, a city in southern Brazil. A dental examination provided information on the prevalence of dental caries (DMFT index). Data about the use of dental service, socioeconomic status, and self-perceived oral health were collected by means of structured interviews. These associations were assessed using Poisson regression models (prevalence ratio; 95% confidence interval). The prevalence of regular use of dental service was 47.8%. Children from low socioeconomic backgrounds and those who rated their oral health as "poor" used the service less frequently. The distribution of the kind of oral healthcare assistance used (public/private) varied across socioeconomic groups. The better-off children were less likely to have used the public service. Clinical, socioeconomic, and psychosocial factors were strong predictors for the utilization of dental care services by schoolchildren.

Resumo em Inglês:

The purpose of this study was to analyze luxation injuries in children between the ages of 0 and 5 years treated at an emergency service department. A total of 1,703 records, corresponding to a period of 10 years at the Emergency Center of the Baby Clinic at Londrina State University, Brazil, were analyzed. The age, gender, etiologic factors, type of injury, injured teeth, treatment and time interval between injury and treatment were determined for each patient. Of the examined records, 409 patients met the study criteria and included a total of 679 injured teeth. Statistical analyses were carried out using the chi-square test with the level of significance set at 5%. Trauma incidence was higher in boys (57.0%) and in children less than two years of age (40.3%). Falling while walking or running was the most predominant etiologic factor (37.7%), and the most prevalent type of injury was subluxation (32.6%). Luxation injuries decreased with increasing age (p = 0.045). Treatment usually occurred within the first 1-15 days and was significantly associated with the type of trauma (p = 0.041). "Monitor only" was the treatment most frequently observed (74.0%). In conclusion, more luxation injuries were found in younger children, predominantly in boys. Falls resulting from walking or running were the etiologic factor most observed, with subluxation as the most common type of trauma. Treatment usually occurred within the first 15 days after the injury. Despite the severity of these injuries, "monitor only" was the eligible treatment.

Resumo em Inglês:

The aim of this study was to quantify and compare the production of transforming growth factor beta (TGF-β), interleukin (IL)-8 and IL-10 by human cultured periodontal ligament and gingival fibroblasts both obtained from the same donors challenged with lipopolysaccharide (LPS) from Porphyromonas gingivalis. Fibroblasts were exposed to 0.1-10 µg/mL of LPS from P. gingivalis and after 24 h the supernatants were collected and analyzed by enzyme-linked immunosorbent assay (ELISA). TGF-β protein production was upregulated in a concentration-dependent manner, mainly in gingival fibroblasts, which was statistically significant when challenged by 10 µg/mL LPS. Additionally, at this concentration, gingival fibroblasts had almost a two-fold increase in the amount of TGF-β when compared to periodontal ligament fibroblasts. Both periodontal ligament and gingival fibroblasts showed an increase in IL-8 production when challenged with 1 µg/mL and 10 µg/mL LPS. IL-10 production remained unaffected when challenged by any of the LPS concentrations tested in either periodontal ligament or gingival fibroblasts. Our results demonstrate that periodontal ligament and gingival fibroblasts when challenged by LPS from P. gingivalis with 24 h may play a critical role in producing TGF-β and IL-8 but not IL-10.

Resumo em Inglês:

The aim of this study was to evaluate the accuracy of three implant transfer impression techniques. Four groups (n = 5) were defined, according to the technique: TC - tapered copings without splint; SC - square copings without splint; SCS - square copings splinted with dental floss and acrylic resin, and CG (control group) - master model with four external hexagonal implants and a superstructure. Individual trays and polyether were used for the impression. All casts were checked for their fit into the master superstructure; for this, all four screws were placed in the implants. Digital photos were taken and images were analyzed using UTHSCSA ImageTool software. Statistical analyses were performed using one-way analysis of variance and Student’s t test (p < 0.05). The means and standard deviation were (µm): CG = 2.03 ± 0.00, TC = 14.74 ± 3.41, SC = 12.08 ± 2.56, and SCS = 6.51 ± 0.09. The control group was found to be statistically different from the TC and SC groups. Within the limitations of this study, all groups presented clinically acceptable standard gap values, and the SCS group showed no statistical difference in relation to the CG (control group), demonstrating more accuracy and fidelity to transfer implants.

Resumo em Inglês:

The aim of this in vitro study was to evaluate the effect of different mouthwashes on superficial roughness and Knoop hardness of two resin composites. Eighty specimens (6 mm Ø and 2 mm height) were prepared and divided into eight experimental groups (n = 10) according to the resin composites (4 Seasons and Esthet X), and storage solutions (G1 - Distilled water; G2 - Colgate Plax Overnight; G3 - Colgate Plax Alcohol Free; and G4 - Colgate Plax Whitening). The initial hardness and roughness readings (T1) were measured and then the specimens were stored in 2 mL of mouthwash for 12 h (T2) and 24 h (T3). The data were analyzed with repeat-measures two-way ANOVA and Tukey's test (α = 5%). Regardless of the type of solution and time of exposure, there was no statistical difference for roughness between the resins (p = 0.44). G4 and G8 presented higher roughness means than G1, G3, G5 and G7, after 12 and 24 hours of immersion. For Knoop microhardness analysis, there was a significant reduction for all groups after 12 hours and 24 hours. We conclude that the mouthwashes containing hydrogen peroxide and/or alcohol decrease the microhardness of the resins tested; however, the mouthwash containing hydrogen peroxide had a higher deleterious effect on roughness.

Resumo em Inglês:

This study evaluated the degree of conversion (DC) and ultimate tensile strength (UTS) of dual-cured resin cements heated to 50º C prior to and during polymerization. Disc- and hourglass-shaped specimens of Rely X ARC (RX) and Variolink II (VII) were obtained using addition silicon molds. The products were manipulated at 25º C or 50º C and were subjected to 3 curing conditions: light-activation through a glass slide or through a pre-cured 2-mm thick resin composite disc, or they were allowed to self-cure (SC). All specimens were dark-stored dry for 15 days. For DC analysis, the resin cements were placed into the mold located on the center of a horizontal diamond on the attenuated total reflectance element in the optical bench of a Fourier Transformed Infrared spectrometer. Infrared spectra (n = 6) were collected between 1680 and 1500 cm-1, and DC was calculated by standard methods using changes in ratios of aliphatic-to-aromatic C=C absorption peaks from uncured and cured states. For UTS test, specimens (n = 10) were tested in tension in a universal testing machine (crosshead speed of 1 mm/min) until failure. DC and UTS data were submitted to 2-way ANOVA, followed by Tukey's test (α= 5%). Both products showed higher DC at 50º C than at 25º C in all curing conditions. No significant difference in UTS was noted between most light-activated groups at 25º C and those at 50º C. VII SC groups showed higher UTS at 50º C than at 25º C (p < 0.05). Increased temperature led to higher DC, but its effects on resin cement UTS depended on the curing condition.

Resumo em Inglês:

The aim of this study was to evaluate the effectiveness of acupuncture in minimizing the severity of radiation-induced xerostomia in patients with head and neck cancer. A total of 24 consecutive patients receiving > 5000 cGy radiotherapy (RT) involving the major salivary glands bilaterally were assigned to either the preventive acupuncture group (PA, n = 12), treated with acupuncture before and during RT, or the control group (CT, n = 12), treated with RT and not receiving acupuncture. After RT completion, clinical response was assessed in all patients by syalometry, measuring the resting (RSFR) and stimulated (SSFR) salivary flow rates, and by the visual analogue scale (VAS) regarding dry mouth-related symptoms. Statistical analyses were performed with repeated-measures using a mixed-effect modeling procedure and analysis of variance. An alpha level of 0.05 was accepted for statistical significance. Although all patients exhibited some degree of impairment in salivary gland functioning after RT, significant differences were found between the groups. Patients in the PA group showed improved salivary flow rates (RSFR, SSFR; p < 0.001) and decreased xerostomia-related symptoms (VAS, p < 0.05) compared with patients in the CT group. Although PA treatment did not prevent the oral sequelae of RT completely, it significantly minimized the severity of radiation-induced xerostomia. The results suggest that acupuncture focused in a preventive approach can be a useful therapy in the management of patients with head and neck cancer undergoing RT.

Resumo em Inglês:

The objective of the current study was to evaluate the sensitivity, specificity and accuracy of fine needle aspiration biopsy (FNAB) of submucous nodules from the oral cavity and head and neck region as an auxiliary diagnostic tool. Fifty patients with nodule lesions in the oral cavity and the head and neck region were selected. All of them were submitted to FNAB and to either incisional or excisional biopsy. The diagnoses from the FNABs were compared with the biopsy diagnosis as the gold standard. All the cases of FNAB were analyzed by a single oral pathologist prior to the biopsy diagnosis. The results showed that the sensitivity of FNAB was 75%, its specificity was 96% and its accuracy was 58.8%. The false positive and false negative rates were 6.7% and 13.3%, respectively. The positive predictive value was 86% and the negative predictive value was 93%. The inconclusive rate was 16/50. FNAB displayed a high success rate for identifying both malignant and benign lesions, but a low accuracy for making a final diagnosis.