Resumo em Inglês:

The aim of this study was to evaluate the bond strength of a resin cement to dentin using different adhesive systems (AS) in the presence or absence of a low-viscosity composite liner (Protect Liner F - PLF) applied over the bonded dentin. The adhesive systems selected were: AdheSE/Vivadent (AD); Clearfil Protect Bond/Kuraray (CP); One-Up Bond F/Tokuyama (OU); Single Bond/3M ESPE (SB); Tyrian SPE/One-Step Plus/Bisco (TY); Xeno III/Dentsply (XE) and Unifil Bond/GC (UN). After removing the labial and lingual enamel surfaces of bovine incisors, dentin fragments were prepared and randomly divided into 15 groups (n = 8). The dentin substrates were bonded with the AS and the PLF was applied or not before application of the resin cement (Panavia F, Kuraray). In the control group, the ED Primer (ED) and the resin cement without PLF were used. The AS, PLF and resin cement tested were used according to the manufacturers' instructions, and all treated dentin surfaces were temporized. After water storage for one week, three cylinders of resin cement were applied to each bonded dentin surface, using tygon tubing molds. The specimens were subjected to micro-shear testing and the data were statistically analyzed (two-way ANOVA, Tukey and Dunnett tests, p < 0.05). The observed mean shear bond strengths in MPa were: ED: 20.2 ± 2.3; AD: 30.3 ± 6.5; CP: 25.3 ± 4.4; OU: 28.3 ± 6.6; SB: 25.6 ± 6.9; TY: 24.5 ± 2.5; XE: 17.3 ± 3.4; UN: 28.4 ± 6.2; AD+PLF: 32.8 ± 4.1; CP+PLF: 29.9 ± 3.9; OU+PLF: 34.1 ± 4.1; SB+PLF: 29.5 ± 8.2; TY+PLF: 29.2 ± 3.9; XE+PLF: 32.8 ± 6.7; UN+PLF: 32.2 ± 4.5. The bond strength of the resin cement to dentin using the tested AS was increased when the low-viscosity composite liner was applied.

Resumo em Inglês:

Color match is one of the most important characteristics of aesthetic restorative materials. Maintenance of color throughout the functional lifetime of restorations is important for the durability of treatment. This characteristic is not constant among dental materials. The purpose of this research was to assess the color stability of five aesthetic restorative materials when immersed in a coffee solution. Seventy-one 17 mm x 1 mm specimens, divided into five groups, were made using one direct composite resin (Tetric Ceram®, Ivoclar/Vivadent - G1), three indirect composite resins (Targis, Ivoclar/Vivadent - G2; Resilab Master, Wilcos - G3; belleGlassTM HP, Kerr - G4) and one porcelain (IPS Empress® 2, Ivoclar/Vivadent - G5). The specimens were immersed in a coffee staining media for 15 days and stored under a controlled temperature of 37°C ± 1°C in the dark. The evaluations were made after 1, 7 and 15 days by means of reflectance spectrophotometry. The data was submitted to two-way ANOVA (p < 0.005) and post hoc tests. Statistical difference was observed between G1 / G3 and the other groups; G2 / G4 and the other groups; and G5 and all the other groups. It was concluded that G1 and G3 showed significantly higher discoloration than the other groups. G2 and G4 showed intermediary pigmentation, while G5 showed the smallest changes.

Resumo em Inglês:

This study compared the coronal and apical leakage of AH Plus with gutta-percha to that of Epiphany with Resilon. Twenty-four single rooted teeth were instrumented and divided into 2 groups according to the solutions for smear layer removal and the obturation materials employed: Group A - 17% EDTA-T and AH Plus with gutta-percha; Group B - primer and Epiphany with Resilon. The Group B specimens were light-cured in the coronal area for 20 s. The external root surfaces were covered with a double layer of ethyl cyanoacrylate, except for the apical foramen and the cavity access. The teeth were immersed in 0.5% methylene blue for 48 h. The specimens were rinsed, dried and axially split for dye penetration measurement with the ImageLab 2.3 software. The t-test showed no significant differences for coronal leakage between the groups, but there were significant differences for apical leakage between the groups (P < 0.05). AH Plus with gutta-percha and Epiphany with Resilon provided the same coronal seal, whereas Epiphany with Resilon provided the best apical seal.

Resumo em Inglês:

The presence of extracellular polysaccharides matrix makes extraction and purification of RNA from Streptococcus mutans within biofilms challenging. In this study, several approaches to purify RNA extracted from S. mutans in suspension cultures and biofilms were examined. The combination of sonication (3 pulses of 30 s at 7 W), suspension in NAES buffer (50 mM sodium acetate buffer, 10 mM EDTA and 1% SDS; pH 5.0) and homogenization-mechanical cells disruption in NAES- acid phenol:chloroform, yielded 9.04 mg (or 0.52 mg) of crude preparation of RNA per 100 mg of total cell (or biofilm) dry-weight. The crude RNA preparations were subjected to various DNAse I treatments. The combination of DNAse I in silica-gel based column followed by recombinant DNase I in solution provided the best genomic DNA removal, resulting in 4.35 mg (or 0.06 mg) of purified RNA per 100 mg of total cell (or biofilm) dry-weight. The cDNAs generated from the purified RNA sample were efficiently amplified using gtfB S. mutans-specific primers. The results showed a method that yields high-quality RNA from both planktonic cells and biofilms of S. mutans in sufficient quantity and quality for real-time RT-PCR analyses.

Resumo em Inglês:

Dentistry is considered a stressful profession, since dentists are exposed to potential stressors during their practice. Therefore, the objective of this study was to identify chronic stress levels and their association with different risk factors among dentists working at public health institutions in Guadalajara, Mexico. The study was observational, cross-sectional and one of association. The universe of this study was composed of 256 dentists that were obtained by means of a census technique. The instrument used for the analysis carried out in the year 2006 was the Stress Syndrome Inventory, performed with concurrent validation. Information was processed for the analysis, and chronic stress levels were identified with a bivariate analysis. Association strength was measured with OR, and confusion factors were controlled with a multivariate logistic analysis. Based on the obtained results, it was concluded that female dentists have a greater risk of developing a high chronic stress level with an adjusted OR of 1.84, meaning that the risk for women is 1.84 times greater than that of men.

Resumo em Inglês:

The purpose of this retrospective study was to analyze the cases of traumatic dental injuries involving root fracture and/or periodontal ligament injury (except avulsion) treated at the Discipline of Integrated Clinic, School of Dentistry of Araçatuba, São Paulo State University (UNESP), Brazil, from January 1992 to December 2002. Clinical and radiographic records from 161 patients with 287 traumatized teeth that had sustained root fracture and/or injuries to the periodontal ligament were examined. The results of this survey revealed that subluxation (25.09%) was the most common type of periodontal ligament injury, followed by extrusive luxation (19.86%). There was a predominance of young male patients and most of them did not present systemic alterations. Among the etiologic factors, the most frequent causes were falls and bicycle accidents. Injuries on extraoral soft tissues were mostly laceration and abrasion, while gingival and lip mucosa lacerations prevailed on intraoral soft tissues injuries. Radiographically, the most common finding was an increase of the periodontal ligament space. The most commonly performed treatment was root canal therapy. Within the limits of this study, it can be concluded that traumatic dental injuries occur more frequently in young male individuals, due to falls and bicycle accidents. Subluxation was the most common type of periodontal ligament injury. Root canal therapy was the type of treatment most commonly planned and performed.

Resumo em Inglês:

The aim of this study was to compare the effectiveness of high speed (HS) and air abrasion (AA) instruments on groups of teeth (deciduous, permanent, bovine), in terms of preparation time, topography and presence of smear layer. Each group consisted of 5 teeth that had their buccal/lingual surfaces prepared by using either HS or AA. All procedures were standardized and timed. The teeth were then sectioned and prepared for evaluation of both the topography and the presence of smear layer by scanning electron microscopy. As regards preparation time, HS yielded preparations 1.5 times quicker than AA did on the three types of dental substrates (Wilcoxon test, p < 0.05). In both techniques (Kruskal-Wallis Test, p < 0.05) the preparation time was influenced by the dental substrate, particularly in deciduous teeth (Mann-Whitney test with Bonferoni's correction, p < 0.017), which required a longer preparation time. In the descriptive analysis of the topography, no difference was found between the substrates. Nonetheless, the different instruments used determined distinctive topographies. Both techniques produced a smear layer (χ2 McNemar, p > 0.05) in all substrates, but with different formations. In conclusion, the HS instrument was found to be more rapid than the AA. No difference was found between the three dental substrates as regards both the topography and the presence of smear layer. The differences found in the present study were only in relation to the effects of each instrument used.

Resumo em Inglês:

The aim of this in vitro study was to evaluate four different approaches to the decision of changing or not defective amalgam restorations in first primary molar teeth concerning the loss of dental structure. Ditched amalgam restorations (n = 11) were submitted to four different treatments, as follows: Control group - polishing and finishing of the restorations were carried out; Amalgam group - the ditched amalgam restorations were replaced by new amalgam restorations; Composite resin group - the initial amalgam restorations were replaced by composite resin restorations; Flowable resin group - the ditching around the amalgam restorations was filled with flowable resin. Images of the sectioned teeth were made and the area of the cavities before and after the procedures was determined by image analysis software to assess structural loss. The data were submitted to ANOVA complemented by the Student Newman Keuls test (p < 0.05). The cavities in all the groups presented significantly greater areas after the procedures. However, the amalgam group showed more substantial dental loss. The other three groups presented no statistically significant difference in dental structure loss after the re-treatments. Thus, replacing ditched amalgam restorations by other similar restorations resulted in a significant dental structure loss while maintaining them or replacing them by resin restorations did not result in significant loss.

Resumo em Inglês:

Through a transversal epidemiological study, conducted with 333 Brazilian children, males (157) and females (176), aged 3 to 6 years old, enrolled in a public preschool, this study aimed to evaluate the prevalence of the different types of vertical interincisal trespass (VIT) and the relationship between these occlusal aspects and anterior lisping and/or anterior tongue thrust in the articulation of the lingua-alveolar phonemes /t/, /d/, /n/ and /l/. All children involved were submitted to a VIT examination and to a speech evaluation. Statistical significance was analyzed through the Qui-square test, at a significance level of 0.05 (95% confidence limit). The quantitative analysis of the data demonstrated the following prevalences: 1 - the different types of VIT: 48.3% for normal overbite (NO), 22.5% for deep overbite (DO), 9.3% for edge to edge (ETE) and 19.8% for open bite (OB); 2 - interdental lisping in relation to the different types of VIT: 42% for NO, 12.5% for DO, 12.5% for ETE, 32.9% for OB; and 3 - children with anterior tongue thrust in the articulation of lingua-alveolar phonemes in relation to the different types of VIT: 42.1% for NO, 14% for DO, 10.5% for ETE, 33.3% for OB. The results demonstrated that there was a significant relationship between open bite and anterior lisping and/or anterior tongue thrust in the articulation of the lingua-alveolar phonemes /t/, /d/, /n/ and /l/; and that there was a significant relationship between deep overbite and the absence of anterior lisping and anterior tongue thrust in the articulation of the lingua-alveolar phonemes.

Resumo em Inglês:

This study aimed to evaluate the effects of a flavor-containing dentifrice on the formation of volatile sulphur compounds (VSCs) in morning bad breath. A two-step, blinded, crossover, randomized study was carried out in 50 dental students with a healthy periodontium divided into two experimental groups: flavor-containing dentifrice (test) and non-flavor-containing dentifrice (control). The volunteers received the designated dentifrice and a new toothbrush for a 3 X/day brushing regimen for 2 periods of 30 days. A seven-day washout interval was used between the periods. The assessed parameters were: plaque index (PI), gingival index (GI), organoleptic breath scores (ORG), VSC levels (as measured by a portable sulphide monitor) before (H1) and after (H2) cleaning of the tongue, tongue coating (TC) wet weight and BANA test from TC samples. The intra-group analysis showed a decrease in ORG, from 3 to 2, after 30 days for the test group (p < 0.05). The inter-group analysis showed lower values in ORG, H1 and H2 for the test group (p < 0.05). There was no difference between the amount of TC between groups and the presence of flavor also did not interfere in the BANA results between groups (p > 0.05). These findings suggest that a flavor-containing dentifrice seems to prevent VSCs formation in morning bad breath regardless of the amount of TC in periodontally healthy subjects.

Resumo em Inglês:

The aim of the present study was to compare quantitatively the distribution of dendritic cell subpopulations in chronic periodontitis and gingivitis. Fourteen biopsies from patients with chronic periodontitis and fifteen from patients with gingivitis were studied. An immunoperoxidase technique was used to quantify the number of Langerhans' cells (CD1a) and interstitial dendritic cells (factor XIIIa) in the oral and sulcular and junctional/pocket epithelia and in the lamina propria. A greater number of factor XIIIa+ dendritic cells in the lamina propria and CD1a+ dendritic cells in the oral epithelium were observed in gingivitis compared to the periodontitis group (p = 0.05). In the sulcular and junctional/pocket epithelia and in the lamina propria, the number of CD1a+ dendritic cells was similar in the gingivitis and periodontitis groups. In conclusion, the number of Langerhans' cells in the oral epithelium and interstitial dendritic cells in the lamina propria is increased in gingivitis compared to periodontitis, which may contribute to the different pattern of host response in these diseases.

Resumo em Inglês:

This study evaluated the effect of mechanical cycling on the bond strength of zirconia posts to root dentin. Thirty single-rooted human teeth were transversally sectioned to a length of 16 mm. The canal preparation was performed with zirconia post system drills (CosmoPost, Ivoclar) to a depth of 12 mm. For post cementation, the canals were treated with total-etch, 3-steps All-Bond 2 (Bisco), and the posts were cemented with Duolink dual resin cement (Bisco). Three groups were formed (n = 10): G1 - control, no mechanical cycling; G2 - 20,000 mechanical cycles; G3 - 2,000,000 mechanical cycles. A 1.6-mm-thick punch induced loads of 50 N, at a 45° angle to the long axis of the specimens and at a frequency of 8 Hz directly on the posts. To evaluate the bond strengths, the specimens were sectioned perpendicular to the long axis of the teeth, generating 2-mm-thick slices, approximately (5 sections per teeth), which were subjected to the push-out test in a universal testing machine at a 1 mm/min crosshead speed. The push-out bond strength was affected by the mechanical cycling (1-way ANOVA, p = .0001). The results of the control group (7.7 ± 1.3 MPa) were statistically higher than those of G2 (3.9 ± 2.2 MPa) and G3 (3.3 ± 2.3 MPa). It was concluded that the mechanical cycling damaged the bond strength of zirconia posts to root dentin.

Resumo em Inglês:

Several studies have reported the benefits of sonic and/or ultrasonic instrumentation for root debridement, with most of them focusing on changes in periodontal clinical parameters. The present study investigated possible alterations in the tensile bond strength of crowns cemented with zinc phosphate cement to natural teeth after ultrasonic instrumentation. Forty recently extracted intact human third molars were selected, cleaned and stored in physiologic serum at 4°C. They received standard preparations, at a 16º convergence angle, and AgPd alloy crowns. The crowns were cemented with zinc phosphate cement and then divided into four groups of 10 teeth each. Each group was then subdivided into two subgroups, with one of the subgroups being submitted to 5,000 thermal cycles ranging from 55 ± 2 to 5 ± 2°C, while the other was not. Each group was submitted to ultrasonic instrumentation for different periods of time: group 1 - 0 min (control), group 2 - 5 min, group 3 - 10 min, and group 4 - 15 min. Tensile bond strength tests were performed with an Instron testing machine (model 4310). Statistical analysis was performed using ANOVA and Tukey's test at the 5% level of significance. A significant reduction in the tensile bond strength of crowns cemented with zinc phosphate and submitted to thermal cycles was observed at 15 min (196.75 N versus 0 min = 452.01 N, 5 min = 444.23 N and 10 min = 470.85 N). Thermal cycling and ultrasonic instrumentation for 15 min caused a significant reduction in tensile bond strength (p < .05).

Resumo em Inglês:

This research evaluated the bone repair process after implantation of homogenous demineralized dentin matrix (HDDM) in surgical defects in the parietal bone of rabbits with alloxan-induced diabetes, using a polytetrafluorethylene (PTFe) barrier for guided bone regeneration. Thirty-six rabbits were used and divided into four groups: control (C, n = 12), diabetic (D, n = 12, left parietal bone), diabetic with PTFe (D-PTFe, same 12 rabbits, right parietal bone), and diabetic with PTFe associated to HDDM (D-PTFe+HDDM, n = 12). Bone defects were created in the parietal bone of the rabbits and the experimental treatments were performed, where applicable. The rabbits were sacrificed after 15, 30, 60 and 90 days. The bone defects were examined radiographically and by optical density (ANOVA and Tukey test, p < .05). The radiographic findings showed that the D-PTFe+HDDM group presented greater radiopacity and better trabecular bone arrangement when compared to that of the C, D and D-PTFe groups. The statistical analysis showed significant differences in the optical density of the newly formed bone among the studied groups. It was possible to conclude that HDDM was biocompatible in diabetic rabbits.

Resumo em Inglês:

Several in vitro studies employ the confection of cavity preparations that are difficult to standardize by means of manual high speed handpieces. This study presents the development of a cavity preparation machine designed to standardize in vitro cavity preparations. A metal base of 25 mm x 25 mm x 4 mm (length x width x height) was coupled to a small mobile table which was designed to be able to move by means of two precision micrometers (0.01-mm accuracy) in the horizontal directions (right-left, and back-front). A high speed handpiece was coupled to a metallic connecting rod which had an accurate dial indicator enabling control of the vertical movement. The high speed handpiece is also able to move 180° around its longitudinal axis and 360° around its transversal axis. The suggested cavity preparation machine precisely helps in the standardization of cavity preparations for in vitro studies.