High-density polyethylene (HDPE) water-proof membranes are used as coatings in vinasse (leachate from sugar cane) storage tanks. The leachate is pumped into the tanks at temperatures of 80-90 °C. Due to these high temperatures and acidity of the waste, these membranes can be degraded, cracked and then loose the function for which they have been designed. This may cause contamination of the soil and groundwater. This study evaluated the effect of vinasse in HDPE membranes after 4 months of exposure in a controlled environment. An aggressive, alkaline pH liquid (sodium hydroxide) was also used. The objective was to evaluate the membrane resistance in contact with acidic and alkaline residues. Physical and mechanical tests, measurement of the carbon black content and thermo gravimetric analysis (TGA) were used to determine degradation of polymer membranes after chemical immersion. While sodium hydroxide resulted caused only minor changes in the physical properties, vinasse induced a thickness change of 7.8%. With immersion in vinasse, an average decrease in strength and deformability (yield) of 34% and 23.5% were measured, respectively. The stiffness increased by 7.8% (average) and the tear strength decreased by 2.7% (average).
HDPE membranes; physical and mechanical properties; carbon black; thermal analysis (TGA)