The number of chain scissions during thermo-degradation of polystyrene under multiple extrusions was calculated. The degradation produces changes in the molecular weight distribution MWD curves. Following the physical meaning of the average molecular weights of a MWD curve it was shown that the number average molecular weight Mn is the only average that can be directly related to the number of molecules in the system. From that it was calculated the number of sectioned chains (ns) as a ratio between the number of chains in the degraded and original polymers. The chain scission distribution function (CSDF) shows that the thermo-mechanical degradation process of polystyrene under multiple extrusions at 240 °C is of a random type, independent of the initial molecular weight.
Thermo-mechanical degradation; extrusion; polistyrene; chain scission