Resumo em Inglês:

This study evaluated the effects of humidity conditions and evaluation times on the dentin bond strength (DBS) of two self-adhesive resin cements (RC). The RC used were: RelyX Unicem (3M ESPE) and Clearfil SA Cement (Kuraray Med.). One hundred and twenty coronal portions of bovine incisors (n = 10) were used. Buccal surfaces were abraded in order to expose a flat dentinal surface (180-grit SiC) and to standardize the smear layer formation (600-grit SiC). The humidity conditions tested were: dry (air-dried for 10 s), slightly moist (water application with disposable applicator on dried dentin and water excess removed with absorbent paper), and moist (same application without water removal). The RC were used according to the manufacturers' recommendations and were applied to prepolymerized resin discs (2 mm thick; Sinfony, 3M ESPE), which were subsequently bonded to the dentin surfaces. After 24 h, half of the teeth were prepared for the microtensile bond strength test, while the other half were stored in water for 6 months and tested in tension (0.5 mm/min) until failure. A 3-way analysis of variance and the Tukey test were performed (preset alpha of 0.05). No RC showed any reduction of DBS after 6 months, and no significant difference was observed between them. The moist dentin increased the bond strength of Clearfil SA Cement for both periods of time. Humidity conditions can change the DBS; however, the study's results were product-dependent.

Resumo em Inglês:

The objective of the study was to measure the marginal and internal fit of zirconia-based all-ceramic three-unit fixed partial dentures (FPDs) (Y-TZP - LAVA, 3M-ESPE), using a novel methodology based on micro-computed tomography (micro-CT) technology. Stainless steel models of prepared abutments were fabricated to design FPDs. Ten frameworks were produced with 9 mm2 connector cross-sections using a LAVATM CAD-CAM system. All FPDs were veneered with a compatible porcelain. Each FPD was seated on the original model and scanned using micro-CT. Files were processed using NRecon and CTAn software. Adobe Photoshop and Image J software were used to analyze the cross-sectional images. Five measuring points were selected, as follows: MG - marginal gap; CA - chamfer area; AW - axial wall; AOT - axio-occlusal transition area; OA - occlusal area. Results were statistically analyzed by Kruskall-Wallis and Tukey's post hoc test (α= 0.05). There were significant differences for the gap width between the measurement points evaluated. MG showed the smallest median gap width (42 µm). OA had the highest median gap dimension (125 µm), followed by the AOT point (105 µm). CA and AW gap width values were statistically similar, 66 and 65 µm respectively. Thus, it was possible to conclude that different levels of adaptation were observed within the FPD, at the different measuring points. In addition, the micro-CT technology seems to be a reliable tool to evaluate the fit of dental restorations.

Resumo em Inglês:

This study evaluated: I) the effect of photo-activation through ceramics on the degree of conversion (DC) and on the Knoop hardness (KHN) of light- and dual-cured resin cements; and II) two different protocols for obtaining the spectra of uncured materials, to determine the DC of a dual-cured resin cement. Thin films of cements were photo-activated through ceramics [feldspathic porcelain (FP); lithium disilicate glass-ceramics of low translucency (e.max-LT), medium opacity (e.max-MO) and high translucency (e.max-HT); glass-infiltrated alumina composite (IC) and polycrystalline zirconia (ZR)] with thicknesses of 1.5 and 2.0 mm. DC was analyzed by Fourier transform infrared (FTIR) spectroscopy. Two protocols were used to obtain the spectra of the uncured materials: I) base and catalyst pastes were mixed, and II) thin films of base and catalyst pastes were obtained separately, and an average was obtained. KHN assessment was performed with cylindrical specimens. The results were analyzed by ANOVA and Tukey's test (α= 0.05). The light-cured cement showed higher DC (61.9%) than the dual-cured cement (55.7%). The DC varied as follows: FP (65.4%), e.max-HT (65.1%), e.max-LT (61.8%), e.max-MO (60.9%), ZR (54.8%), and IC (44.9%). The light-cured cement showed lower KHN (22.0) than the dual-cured (25.6) cement. The cements cured under 1.5 mm spacers showed higher KHN (26.2) than when polymerized under 2.0 mm ceramics (21.3). Regarding the two protocols, there were significant differences only in three groups. Thus, both methods can be considered appropriate. The physical and mechanical properties of resin cements may be affected by the thickness and microstructure of the ceramic material interposed during photo-activation.

Resumo em Inglês:

The aim of this study was to determine the degradation resistance of three new formulations-silorane-, Ormocer- and dimer-acid-based materials-and compare them to the traditional dimethacrylate-based materials. One silorane- (Filtek P90, P90), one Ormocer- (Ceram-X, CX), one dimer-acid- (N'Durance, ND) and two dimethacrylate-based (Filtek P60, P60; Tetric Ceram, TC) materials were investigated. Water sorption (Wsp) and solubility (Wsl) were determined after the materials were immersed in water for 28 days. Knoop hardness (KH) was determined before and after 24 h immersion in pure ethanol. The flexural-strength (FS) was determined by the bending test after one-week storage in a dry environment or after one-week immersion in pure ethanol. Data were submitted to analysis of variance (ANOVA) and Tukey's test (95%). The three new formulations showed lower Wsp than the dimethacrylate-based formulation. CX (0.50 ± 0.17%) and ND (0.72 ± 0.19%) exhibited the lowest Wsp, whereas P90 (0.02 ± 0.03%) and P60 (0.04 ± 0.03%) showed the lowest Wsl. All resins showed reduced Knoop hardness number (KHN) after ethanol immersion. P60 presented the lowest decrease in KH value (19 ± 5%). TC (48 ± 3%) and P90 (39 ± 9%) showed the highest KHN decrease after ethanol storage. The FS of CX, ND and TC were affected by ethanol storage. The new formulations did not improve the degradation resistance, as compared with the traditional methacrylate-based materials.

Resumo em Inglês:

Pulpotomy in deciduous teeth is a controversial issue, especially with regard to alternative materials used for the direct pulp capping of the root canal pulp tissue. The aim of the present study was to perform a histological analysis of the initial reaction of the root canal pulp tissue in rats, following pulpotomy and pulp capping with (1) green propolis extract, (2) iodoform paste, (3) green propolis extract + iodoform and (4) calcium hydroxide paste with saline solution. Analyses were performed after 24 hours, 72 hours and 7 days. The substances containing green propolis extract and iodoform led to the production of an intense inflammatory infiltrate and necrosis in the root canal pulp tissue throughout the analyses. In the calcium hydroxide group, inflammatory infiltrate only prevailed at the 72-hour evaluation. Among the substances tested, calcium hydroxide paste induced the lowest intensity of inflammatory response in the root canal pulp tissue. Longer studies should be carried out to analyze the pulp repair process following pulpotomy and pulp capping with the compounds analyzed.

Resumo em Inglês:

Few articles have shown changes in bone metabolism caused by hypertension. The objective of this study was to investigate the relationship between hypertension and bone healing. Circular critical-size defects 5 mm and 2 mm in diameter were created, respectively, on the left and right side of the mandible in 40 spontaneously hypertensive and 40 control Wistar-Kyoto rats. Five animals from each strain were killed 2, 3, 5, 10, 15, 30, 60 and 90 days after surgery. The macroscopic evaluation showed great mandibular angle deformation on the left side and non-healed defects on both sides and groups. Histological evaluation revealed similar bone healing on both sides, with initial necrosis in the central area, and fibrosis and angiogenesis within the first 5 days. From the 10th postoperative day on, the newly formed bone displayed progressive thickening until the 90th postoperative day, when the defect margins presented a compact bone structure. Furthermore, the statistical analysis of the histometric data did not reveal any significant hypertension effect on bone healing in the defect area. These results suggest that bone healing was not different between spontaneously hypertensive rats and control rats.

Resumo em Inglês:

Assessment of the maxillary sinus anatomy before sinus augmentation is important for avoiding surgical complications, because of the close anatomical relationship between the posterior maxillary teeth and the maxillary sinus. The posterior superior alveolar artery (PSAA) is the branch of the maxillary artery that supplies the lateral sinus wall and overlying membrane. We evaluated the location of the PSAA and its relationship to the alveolar ridge and maxillary sinus using cone beam computed tomography (CBCT). The study group consisted of 135 CBCT scans (270 sinuses) obtained from the archive of the dentomaxillofacial radiology department at Yeditepe University Faculty of Dentistry, Istanbul, Turkey. The distance between the lower border of the artery and the alveolar crest, bone height from the sinus floor to the ridge crest, distance from the artery to the medial sinus wall, and the diameter and location of the artery were determined. The occurrence of septa and pathology were recorded from CBCT scans. The PSAA was observed in 89.3% of sinuses, and 71.1% of arteries were intraosseous with diameters mostly < 1 mm (68.9%). The prevalence of sinus septa was 55.2%, and that of sinus pathology was 57.4%. The mean age was 43.07 ± 17.55 years. There was a statistically significant difference between the location of the artery and gender (p < 0.05). The prevalence of sinus membrane thickening was 57.4%. Detailed knowledge about the location of the PSAA and sinus morphology may be obtained with CBCT before maxillary sinus surgery.

Resumo em Inglês:

Primary teeth are interesting models that can be used to study physiological and pathological processes involving cells and extracellular matrices in hard and soft tissues. This study investigated the expression and distribution of biglycan and decorin-the non-collagenous components of the extracellular matrix-in primary teeth tissue, during physiological root resorption. Thirty healthy human primary teeth were grouped together according to root length: Group I - two-thirds root length, Group II - one-third root length, and Group III - teeth with no root. The streptavidin-biotin-peroxidase immunohistochemical method was used with antibodies against the previously named antigens. The proteoglycans studied were found in the pulp and dentin extracellular matrix in all groups without any differences in the proteins, among the groups. Biglycan was observed mainly in predentin and in pulp connective tissue in the resorption area. In addition, decorin was observed mainly in pulp connective tissue, but near the resorption area. Biglycan and decorin were distributed differentially in the dental tissues. The present immunohistocytochemical data, combined with previously reported data, suggest that these proteoglycans could be involved in regulating the physiological resorption process in healthy primary teeth.