Passivity of Conventional and CAD/CAM Fabricated Implant Frameworks

The objective of this research was to evaluate the passivity by measuring the passive fit and strain development of frameworks screwed on abutments, made by CAD/CAM technology, and to compare these parts with samples manufactured by conventional casting. Using CAD/CAM technology, four samples were made from zirconia (Zircad) and four samples were manufactured from cobalt-chrome (CoCrcad). The control groups were four specimens of cobalt-chrome, made by one-piece casting (CoCrci), with a total of 12 frameworks. To evaluate the passive fit, the vertical misfit at the abutment-framework interface was measured with scanning electron microscopy (250×) when only one screw was tightened. The mean strain in these frameworks was analyzed by photoelasticity test. A significant difference in the passive fit was observed between the control and sample groups. CoCrcad exhibited the best value of passive fit (48.76±13.45 µm) and CoCrci the worst (187.55±103.63 µm); Zircad presented an intermediate value (103.81±43.15 µm). When compared to the other groups, CoCrci showed the highest average stress around the implants (17.19±7.22 kPa). It was concluded that CAD/CAM-fabricated frameworks exhibited better passivity compared with conventionally fabricated frameworks. CAD/CAM-fabricated Co-Cr frameworks may exhibit better passive fit compared with CAD/CAM-fabricated zirconia frameworks. Even so, similar levels of stress were achieved for CAD/CAM-fabricated frameworks.

dental implants; dental prosthesis; computer-aided design/computer-aided manufacturing